Journal of Applied Polymer Science   2016 年 133 卷 32 期

2016.08.20

In the present study, regenerated cellulose membrane with "imprinted morphology" and low crystallinity was fabricated from the crystal cellulose/[Bmim]Cl solution. Spherulites of 1-butyl-3-methilimidazolium chloride ([Bmim]Cl) and cellulose/[Bmim]Cl solution were observed using polarized optical microscopy under certain condition. The fabricated cellulose membranes presented some particular characteristics compared with the membrane prepared from traditional cellulose/[Bmim]Cl solution. All the fabricated membranes were characterized by optical microscope, Wide-angle X-ray diffraction (WAXD), thermo-gravimetric analysis, and mechanical testing. The images showed that the resulting membranes prepared from crystal cellulose/[Bmim]Cl solution were "imprinted" with patterns which originated from the crystalline structure of [Bmim]Cl. The results of WAXD showed that the obtained cellulose membrane exhibited low diffraction peaks and crystallinity of approximately 24.57%. Furthermore, the low crystallinity led to the low mechanical property (27.5 MPa), thermal stability (315.4 ?°C), and high moisture regain (9.5%).